These plates guarantee suitability for cold forming because of their technological processing. Standard methods used for processing these plates are bending, fl anging, cold roll forming, etc. Based on agreement these plates can be delivered in the condition suitable for hot-dip zinc-coating.

Designation		Min. Yield Strength ReH [MPa]	Tensile Strength Rm [MPa]	Min. Elongation [%]	Min. Impact Energy KV 1) [°C/J] - longitudinal	Transverse Bend Test 2)	Dimension Table No.	Max. Thickness [mm]
S260NC		260	370-490	30	-20/40	0 t	table 1	20 3)
S315NC		315	430-550	27	-20/40	0,5 t	table 1	20 3)
S355NC		355	470-610	25	-20/40	0,5 t	table 1	20 3)
S420NC		420	530-670	23	-20/40	0,5 t	table 2	20 3)

Maximum value of the carbon equivalent as per the formula   on agreement
1) Testing on agreement
2) Minimum former diameter for 180° bend angle; t – plate thickness
3) Under standard